[KMg3(AlSi3O10)F2] -Synthetized Fluorphlogopite Mica, 8x 8x0.2 thick (mm), as cleaved Orientation 0001 30 CO32-

30  CO32-

Hardness:  9 ( mohs)

1mm (Thickness)

Orientation: Y-cut with 36 degree off

Mobility:                                    (1600 - 2130) cm^2/V

[KMg3(AlSi3O10)F2] -Synthetized Fluorphlogopite Mica, 8x 8x0.2 thick (mm), as cleaved Orientation 0001 30 CO32-Synthetic fluorophlogopite is obtained by cooling and devitrification of chemical raw materials by high temperature melting. The single wafer fraction is KMg3(AlSi3O10)F2, which belongs to the monoclinic system and is a typical layered silicate. KMg3(AlSi3O10)F2 is a typical layered silicate. Many of its properties are superior to natural mica. For example, when the temperature is higher than 1200C, the volume resistivity of synthetic fluorophlogopite